LNP™THERMOCOMP™ Compound 9X02841

SI

| British

| Metric

| PDF

Americas: COMMERCIAL

LNP* Thermocmop* 9X02841 is a PBT/Polycarbonate blend containing proprietary fillers.

Property

MECHANICAL

Tensile Stress, yld, Type I, 5 mm/min

840

kgf/cm²

ASTM D 638

Tensile Stress, brk, Type I, 5 mm/min

840

kgf/cm²

ASTM D 638

Tensile Strain, yld, Type I, 5 mm/min

2.7

%

ASTM D 638

Tensile Strain, brk, Type I, 5 mm/min

2.7

%

ASTM D 638

Tensile Modulus, 50 mm/min

52200

kgf/cm²

ASTM D 638

Flexural Stress, yld, 1.3 mm/min, 50 mm span

1290

kgf/cm²

ASTM D 790

Flexural Stress, brk, 1.3 mm/min, 50 mm span

1250

kgf/cm²

ASTM D 790

Flexural Modulus, 1.3 mm/min, 50 mm span

46900

kgf/cm²

ASTM D 790

Tensile Stress, yield, 5 mm/min

80

MPa

ISO 527

Tensile Stress, break, 5 mm/min

80

MPa

ISO 527

Tensile Strain, yield, 5 mm/min

2.6

%

ISO 527

Tensile Strain, break, 5 mm/min

2.6

%

ISO 527

Tensile Modulus, 1 mm/min

4880

MPa

ISO 527

Flexural Stress

115

MPa

ISO 178

Flexural Modulus, 2 mm/min

4480

MPa

ISO 178

IMPACT

Izod Impact, unnotched, 23°C

53

cm-kgf/cm

ASTM D 4812

Izod Impact, notched, 23°C

7

cm-kgf/cm

ASTM D 256

Multiaxial Impact

45

cm-kgf

ISO 6603

Instrumented Impact Total Energy, 23°C

171

cm-kgf

ASTM D 3763

Izod Impact, unnotched 80*10*4 +23°C

31

kJ/m²

ISO 180/1U

Izod Impact, notched 80*10*4 +23°C

7

kJ/m²

ISO 180/1A

THERMAL

HDT, 0.45 MPa, 3.2 mm, unannealed

141

°C

ASTM D 648

HDT, 1.82 MPa, 3.2mm, unannealed

115

°C

ASTM D 648

CTE, -30°C to 30°C, flow

4.1E-05

1/°C

ASTM D 696

CTE, -30°C to 30°C, xflow

6.3E-05

1/°C

ASTM D 696

HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm

140

°C

ISO 75/Bf

HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm

115

°C

ISO 75/Af

PHYSICAL

Density

1.33

g/cm³

ASTM D 792

Moisture Absorption, 50% RH, 24 hrs

0.09

%

ASTM D 570

Mold Shrinkage, flow, 24 hrs (5)

0.4 - 0.6

%

ASTM D 955

Mold Shrinkage, xflow, 24 hrs (5)

0.6 - 0.8

%

ASTM D 955

Density

1.33

g/cm³

ISO 1183

Moisture Absorption (23°C / 50% RH)

0.14

%

ISO 62

Source GMD, last updated:2008/11/21

Processing

Injection Molding

Drying Temperature

120

°C

Drying Time

4

hrs

Maximum Moisture Content

0.05

%

Melt Temperature

240 - 265

°C

Front - Zone 3 Temperature

260 - 270

°C

Middle - Zone 2 Temperature

245 - 255

°C

Rear - Zone 1 Temperature

220 - 230

°C

Mold Temperature

80 - 100

°C

Back Pressure

0.2 - 0.3

MPa

Screw Speed

30 - 60

rpm